This study challenged to improve the resistance against hydrogen embrittlement by increasing the concentration of carbon segregated at prior austenite grain boundary (PAGB), XPAGB, in low-carbon martensitic steels. The specimens with/without carbo...
The present study investigated the hydrogen-related fatigue fracture under various test frequencies in low-carbon martensitic steel. In the hydrogen-charged specimen, although the number of cycles to failure decreased with decreasing test frequenc...
A typical hydrogen-related transgranular fracture, namely quasi-cleavage fracture, is usually accompanied by serrated markings on the resultant fracture surfaces in steels with body-centered cubic phases. The present paper investigated the microsc...
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY 46(75) 37509-37517 2021年10月
This study investigated the hydrogen-related fatigue fracture in 2Mn-0.1C steel having a lath martensite microstructure. The presence of hydrogen significantly reduced the fatigue life. The transgranular surface was a main component in each stress...