PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS 469(15-20) 1307-1310 2009年8月 [査読有り]
GdBa2Cu3Oy(GdBCO) films were fabricated on pulsed laser deposition (PLD)-CeO2/ion-beam-assisted deposition (IBAD)-Gd2Zr2O7/HasteIloy C276 metal substrate tapes using the continuous in-plume PLD method. The control of the target composition is impo...
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS 469(15-20) 1329-1331 2009年8月 [査読有り]
YBa(2)Cu(3)O(7-y) (YBCO) long tapes derived from the metal-organic deposition (MOD) method using the starting solution containing trifluoroacetate (TFA) have been developed with high critical currents (I(c)) over 200 A/cm-width. However, high spee...
R. Teranishi   K. Tada   J. Yoshida   K. Yamada   N. Mori   M. Mukaida   M. Inoue   T. Kiss   K. Nakaoka   M. Miura   M. Yoshizumi   T. Izumi   Y. Shiohara   
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS 469(15-20) 1345-1348 2009年8月 [査読有り]
YBa2Cu3O7-delta (YBCO) films were grown by using precursor films with barium concentration gradient in film thickness by an advanced metal organic deposition process using trifluoroacetates (TFA-MOD). We have reported previously that a lot of non-...
R. Teranishi   A. Mitani   K. Yamada   N. Mori   M. Mukaida   M. Miura   K. Nakaoka   T. Izumi   Y. Shiohara   
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS 469(15-20) 1349-1352 2009年8月 [査読有り]
YBa(2)Cu(3)O(y) (YBCO) films grown by starting solutions with Ba-poor (Y:Ba:Cu = 1: 1.53, Ba/Y = 1.5) have been reported to perform higher J(c) than that for YBCO films with stoichiometric one due to smaller and less pores in YBCO films by metal o...
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS 469(15-20) 1326-1328 2009年8月 [査読有り]
We have developed a new starting solution consisting of non-fluorine (F-free) yttrium salt, barium trifluoroacetate and copper octylate with focusing on a high-speed production of YBa(2)Cu(3)O(7-y) (YBCO) coated conductors by the trifluoroacetate-...