JOURNAL OF THE JAPAN INSTITUTE OF METALS 75(10) 582-591 2011年10月 [査読有り]
Changes in microstructures at recovery stage after cold-rolling at 50% reduction rate were observed in an Al-Mg-Si alloy by means of SEM-EBSD system. The same area in the specimen was observed before and after cold-rolling. Intermittent annealing ...
JOURNAL OF THE JAPAN INSTITUTE OF METALS 75(10) 575-581 2011年10月 [査読有り]
Microstructural changes in an Al-Mg-Si alloy during annealing at 673 K after cold-rolling with a 50% reduction rate were observed. An alloy specimen was repeatedly subjected to intermittent annealing using a salt bath, Ar ion-polishing, and observ...
Recrystallization phenomena in an Al-Mg-Si alloy cold-rolled at 30 and 50% reduction rates were observed on the same area in specimens during annealing at 673 K using SEM-EBSD method. After recovery in a narrow sense occurred, coarse subgrain micr...